HIGH FORM CRUCIBLE
Labwares are made by slip casting and pressure casting. Purity of sintered Alumina to be above 99.7%. Sintered Grain Size is between 2-4 microns. Sintered Density: above 3.9 gm/cc, above 98% TD (3.96gm/cc). Thermal Shock Behaviour: Temperature change rate should not exceed 150 °C/Hr. Maximum Temperature of use without load: 1750°C. Alumina High Form Crucible tested for Ultra High Vacuum Compatibility.
LARK Catalog No. | Capacity (ml) | Size OD (mm) | Height (mm) |
LACHF-5 | 5 | 23 | 28 |
| LACHF-10 | 10 | 29 | 33 |
| LACHF-20 | 20 | 40 | 35 |
| LACHF-50 | 50 | 51 | 47 |
| LACHF-100 | 100 | 60 | 62 |
| LACHF-250 | 250 | 82 | 93 |